Khoom siv:Chromium. Purity:99.99%. Melting Point:Xyoo 1907 degree. Boiling Point:2672 degree. Qhov tsos:Grey pellets. Theoretical ntom ntom:7.18g / cm³. Coefficient ntawm Thermal Expansion:4.9 x
Khoom siv:Mo1/Mo-la/TZM. Thickness:0.3mm-2.0 hli. Ntev:50mm-200 hli. Dav:10mm-50 hli. Qhov tob:10mm-30 hli. Ceev:10.2g / cm³. Nto:Sintered / Polished / Sib Tsoo. Melting Point:2623 degree.
Khoom siv:Tantalum (Ta). Purity:3N 99.9% | 3N5 99.95% | 4N 99.99% | 4N5 99.995%. Ceev:16.6 g / cm³. Boiling Point:5 425de. Melting Point:3017 degree. Qhov tsos:Hlau grey metallic khoom. Surface
Cov ntsiab lus tungsten:90% - 97% wt. Ceev:16.5 - 18.75 g/cm³. Nto Roughness:Ra 0.4 - Ra 3.2 μm. Hardness:24 - 36 HRC. Tensile zog:700 - 1050 MPa. Dimensional kam rau ua:± 0.05 hli. Khoom Qib:Chav
Khoom siv:92.5 wb. Txoj kab uas hla:4-20 hli. Ntev:300-2000 hli. Ceev:17.5 g / cm³. Tensile zog:793mpa ua. Hardness:26 HRC. Nto:Grinded / Polished / Bright. Txheem:ASTM B777 Cov khoom lag luam. Lub
Khoom siv:Mo/Mo-La/TZM. Purity:Ntau dua lossis sib npaug li 99.95%. Loj:5-300 hli. Ceev:10.2 g / cm³. Thickness:0.1-5 hli. Nto:Polished, Ra Tsawg dua los yog sib npaug rau 0.8 μm. Melting Point:2617
Khoom siv:C276. Loj:M6-M20. Ceev:8.89-8.90g / cm³. Tensile zog:690-790MPa. Hardness:100-150 HB. Nto:Polishing. MOQ:2 Pcs. Txheem:ASTM B574 / DIN 125 / EN 10204-3.1. Lub sij hawm xa tuaj:25-30 HNUB.
Khoom siv:Ir. Purity:Ntau dua lossis sib npaug li 99.95%. Txoj kab uas hla:0.5mm-20mm (Customizable). Ntev:50-1000 hli. Ceev:Ntau dua lossis sib npaug li 22.62g / cm³. Tensile zog:900-1200MPa.
Khoom siv:Tungsten. Purity:Ntau dua lossis sib npaug li 99.95%. Ceev:Ntau dua lossis sib npaug rau 17.0 - 18.5 g/cm³. Txoj kab uas hla:1 hli-200mm. Melting Point:3410 degree. Tensile zog:900-1200MPa.
Khoom siv:Tungsten. Purity:Ntau dua lossis sib npaug li 99.95%. Ceev:Ntau dua lossis sib npaug li 18.2 g / cm³. Loj:8 x 60 mm. Melting Point:3410 degree. Tensile zog:900-1200MPa. Hardness:HRC 25-35.
Khoom siv:Ir. Purity:Ntau dua lossis sib npaug rau 99.99% (4N). Ceev:22.56 g / cm³. Txoj kab uas hla:Φ Ntau dua lossis sib npaug li 20mm. Thickness:1-15mm lossis customized. Dav:10-150 hli.
Khoom siv:Qib 5 / Ti-6Al-4V. Ceev:4.43 g / cm³. Thickness:0.5-20mm lossis customized. Dav:1000-2500 hli. Ntev:2000-6000mm. Melting Point:1650 degree. Tensile zog:895-930MPa. Nto:Sib tsoo, Polishing.